Dielectric structure in nonvolatile memory device and method for fabricating the same

ABSTRACT

A dielectric structure in a nonvolatile memory device and a method for fabricating the same are provided. The dielectric structure includes: a first oxide layer; a first high-k dielectric film formed on the first oxide layer, wherein the first high-k dielectric film includes one selected from materials with a dielectric constant of approximately 9 or higher and a compound of at least two of the materials; and a second oxide layer formed on the first high-k dielectric film.

FIELD OF THE INVENTION

The present invention relates to a semiconductor memory device and a method for fabricating the same; and, more particularly, to a dielectric structure such as an inter poly dielectric (IPD) or an inter poly oxide (IPO), which exists between a floating gate and a control gate in a nonvolatile memory device, and a method for fabricating the same.

DESCRIPTION OF RELATED ARTS

Unlike a dynamic random access memory (DRAM) device, a flash memory device, which is a nonvolatile memory device, does not require a capacitor device. Instead, the flash memory device requires an electric charge storage space to read and write data. To perform such read and write operations, a ratio between entire capacitance including capacitance formed in a tunnel oxide layer and capacitance of a dielectric structure such as an inter-poly dielectric (IPD) or an inter-poly oxide (IPO) existing between a floating gate and a control gate must be satisfied.

However, as semiconductor devices are becoming highly integrated, a conventional oxide/nitride/oxide (ONO) structure shows limitations in securing enough capacitance. If the thickness of the ONO structure is reduced to secure the capacitance, a leakage current characteristic becomes deteriorated. As a result, introducing a material with a high dielectric constant is inevitable. However, if a high-k dielectric film is used as a single layer, the coupling ratio may become difficult to control. Therefore, a material with an appropriate dielectric constant is required.

SUMMARY OF THE INVENTION

It is, therefore, an object of the present invention to provide a dielectric structure of a nonvolatile memory device and a method for fabricating the same, wherein the dielectric structure is capable of: satisfying a required level of the coupling ratio in accordance with the decreasing design rule as memory devices have become highly integrated; securing a superior leakage current characteristic; and improving reliability.

In accordance with an aspect of the present invention, there is provided a dielectric structure in a nonvolatile memory device including a floating gate, the dielectric structure and a control gate, the dielectric structure including: a first oxide layer; a first high-k dielectric film formed on the first oxide layer, wherein the first high-k dielectric film includes one selected from materials with a dielectric constant of approximately 9 or higher and a compound of at least two of the materials; and a second oxide layer formed on the first high-k dielectric film.

In accordance with another aspect of the present invention, there is provided a method for fabricating a dielectric structure of a nonvolatile memory device, wherein the nonvolatile memory device includes a floating gate, the dielectric structure and a control gate, the method including: forming a first oxide layer on the floating gate; forming a first high-k dielectric film on the first oxide layer, wherein the first high-k dielectric film includes one selected from materials with a dielectric constant of approximately 9 or higher and a compound of at least two of the materials; and forming a second oxide layer on the first high-k dielectric film.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other objects and features of the present invention will become better understood with respect to the following description of the specific embodiments given in conjunction with the accompanying drawings, in which:

FIG. 1 is a cross-sectional view illustrating a dielectric structure in accordance with a first embodiment of the present invention;

FIG. 2 is a graph illustrating a dielectric characteristic of a hafnium oxide-aluminum oxide (HfO₂—Al₂O₃)-based thin film;

FIG. 3 is a cross-sectional view illustrating a dielectric structure in accordance with a second embodiment of the present invention;

FIGS. 4A to 4E are cross-sectional views illustrating a method for fabricating the dielectric structure in accordance with the first embodiment of the present invention;

FIGS. 5 to 7 are flow diagrams illustrating a method for fabricating a high-k dielectric film using an atomic layer deposition (ALD) method in accordance with a specific embodiment of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

A dielectric structure of a nonvolatile memory device and a method for fabricating the same in accordance with specific embodiments of the present invention will be described in detail with reference to the accompanying drawings. Also, regarding the drawings, illustrated thicknesses of layers and regions are exaggerated for definitude. When a first layer is referred to as being on a second layer or “on” a substrate, it could mean that the first layer is formed right on the second layer or the substrate, or it could also mean that a third layer may exit between the first layer and the substrate. Furthermore, identical reference numerals throughout the specific embodiments of the present invention represent identical elements.

FIG. 1 is a cross-sectional view illustrating a gate electrode in a flash memory device in accordance with a first embodiment of the present invention. Herein, the gate electrode has a stack structure and is illustrated as an example to describe a dielectric structure in a nonvolatile memory device.

Referring to FIG. 1, the dielectric structure 16 of the nonvolatile memory device is formed with a layered structure of: a first oxide layer 16A, a high-k dielectric film 16B and a second oxide layer 16C.

The first oxide layer 16A and the second oxide layer 16C are high temperature oxide layers, which are formed in a thickness ranging from approximately 30 Å to approximately 60 Å by employing superior internal pressure and dichlorosilane (SiH₂Cl₂) and hydrogen oxide (H₂O) gases both having a superior time dependent dielectric breakdown (TDDB) characteristic. Furthermore, the high-k dielectric film 16B is formed by employing a material with a dielectric constant of equal to or greater than approximately 9 or a compound of such materials with an appropriate feeding ratio.

In an article by G. D. Wilk et al. (Journal of Applied Physics, vol. 89 (10), pp. 5243-5275, 2001), such dielectric materials and their characteristics are disclosed. Table 1 shows this disclosure in detail.

TABLE 1 Dielectric Band gap Material constant (k) Eg(eV) Crystal structure(s) SiO₂ 3.9 8.9 Amorphous Si₃N₄ 7 5.1 Amorphous Al₂O₃ 9 8.7 Amorphous Y₂O₃ 15 5.6 Cubical La₂O₃ 30 4.3 Hexagonal, Cubical Ta₂O₅ 26 4.5 Orthorhombic TiO₂ 80 3.5 Tetragonal (rutile, anatase) HfO₂ 25 5.7 Monoclinic, Orthorhombic, Cubical ZrO₂ 25 7.8 Monoclinic, Orthorhombic, Cubical

As shown in Table 1, the high-k dielectric film 16B is formed by employing one from a group consisting of aluminum oxide (Al₂O₃), yttrium oxide (Y₂O₃), lanthanum oxide (La₂O₃), tantalum oxide (Ta₂O₅), titanium oxide (TiO₂), hafnium oxide (HfO₂), and zirconium oxide (ZrO₂). Preferably, one of Al₂O₃, Y₂O₃, HfO₂, and ZrO₂ with a dielectric constant ranging from approximately 9 to 25 is used. Meanwhile, a dielectric constant of La₂O₃, Ta₂O₅, and TiO₂ ranges from approximately 26 to 80. The high-k dielectric film 16B is also formed by employing a compound of two chosen from a group consisting of Al₂O₃, Y₂O₃, La₂O₃, Ta₂O₅, TiO₂, HfO₂, and ZrO₂ with appropriate feeding ratio. For example, the high-k dielectric film 16B is formed by employing one compound from a group consisting of HfO_(x)Al_(y)O_(z), ZrO_(x)Al_(y)O_(z) and LaO_(x)Al_(y)O_(z). Herein, x, y and z are 0 or natural numbers, representing feeding ratios of atoms composing the individual compounds.

For example, as shown in FIG. 2, the dielectric constant of HfO_(x)Al_(y)O_(z) can be controlled to be within a range of approximately 9 to 20 according to the feeding ratio, that is, a mixing rule. Therefore, instead of a nitride-based layer, HfO_(x)Al_(y)O_(z) with a controlled thickness and feeding ratio can be interpositioned in a dielectric structure of a conventional ONO structure to satisfy electrical and physical characteristics such as a leakage current.

As described above, it is preferable to use an HfO₂—Al₂O₃-based thin film with superior step coverage, which allows an easy dielectric constant control to satisfy a physical thickness limit and an electrical oxide thickness (EDT) required by each device, as well as a leakage current characteristic.

As shown in FIG. 2, the HfO₂—Al₂O₃-based thin film can convert the dielectric constant freely within a range of approximately 9 to 20 according to the feeding ratio, that is, the mixing rule. However, if only a single high-k dielectric structure is used instead of the ONO layer, the dielectric constant becomes too high, and the coupling ratio cannot be controlled. Thus, the Hfo₂-Al₂O₃-based thin film with an appropriate thickness and feeding ratio is inserted in the ONO layer structure instead of the nitride-based layer, to satisfy electrical and physical characteristics required by the device. On the other hand, the reference numerals 10, 12, 14, and in FIG. 1 which are not described above, represent a substrate, a tunnel oxide layer, a first polysilicon layer for use in a floating gate, and a second polysilicon layer for use in a control gate, respectively.

FIG. 3 is a cross-sectional view illustrating a gate electrode of a flash memory device in accordance with a second embodiment of the present invention. Herein, the gate electrode has a stack structure and is illustrated as an example to describe a dielectric structure of a nonvolatile memory device.

Referring to FIG. 3, different from the dielectric structure 16 in FIG. 1, the dielectric structure 26 of the nonvolatile memory device is formed with a layered structure of: a first oxide layer 26A, a first high-k dielectric film 26B, a second oxide layer 26C, a second high-k dielectric film 26D, and a third oxide layer 26E. The first oxide layer to the third oxide layer 26A, 26C and 26D of the dielectric structure are high temperature oxide layers formed as described in the first embodiment. Furthermore, the first high-k dielectric film 26B and the second high-k dielectric film 26D are formed of a material identical to the high-k dielectric film 16B described in the first embodiment, or a compound of such materials.

Hereinafter, a method for fabricating the dielectric structure of the nonvolatile memory device in accordance with the first embodiment is described with reference to FIGS. 4A to 4E.

As shown in FIG. 4A, the tunnel oxide layer 12 (or a gate oxide layer) is formed on the substrate 10 whereon a semiconductor structure is formed through a series of fabrication processes. Herein, the tunnel oxide layer 12 is formed by employing a dry oxidation method or a wet oxidation method. For example, the wet oxidation method forms the tunnel oxide layer 12 by performing a wet oxidation process at a temperature ranging from approximately 750° C. to approximately 800° C. and then performing an annealing process for approximately 20 minutes to approximately 30 minutes in nitrogen (N₂) atmosphere at a temperature ranging from approximately 900° C. to approximately 910° C.

Meanwhile, the semiconductor structure includes a device isolation region formed by a shallow trench isolation (STI) process and a well region formed by an ion implantation process.

Subsequently, the first polysilicon layer 14 for a floating gate is formed on the tunnel oxide layer 12. Herein, the first polysilicon layer 14 is formed by employing one of doped polysilicon and undoped polysilicon. For example, the first polysilicon layer 14 can be formed in a thickness ranging from approximately 500 Å to approximately 2,000 Å by a low pressure chemical vapor deposition (LPCVD) method using silane (SiH₄) or disilane (Si₂H₆) and phosphine (PH₃) gases. Herein, it is preferable to form the first polysilicon layer 14 with a minimized grain size. For example, the first polysilicon layer 14 is formed at a temperature ranging from approximately 580° C. to approximately 620° C. with a low pressure ranging from approximately 0.1 Torr to approximately 3 Torr.

Furthermore, the first oxide layer 16A is formed on the first polysilicon layer 14. Herein, the first oxide layer 16A is a high temperature oxide layer formed in a thickness ranging from approximately 30 Å to approximately 60 Å by employing a superior internal pressure and SiH₂Cl₂ and H₂O gases as source gases with a superior TDDB characteristic.

Then, as shown in FIG. 4B, the high-k dielectric film 16B is formed on the first oxide layer 16A using an atomic layer deposition (ALD) method with superior step-coverage. Herein, the high-k dielectric film 16B is an HfO₂—Al₂O₃-based thin film, formed in a thickness ranging from approximately 30 Å to approximately 100 Å. A feeding ratio of hafnium (Hf) to aluminum (Al) in the HfO₂—Al₂O₃-based thin film ranges from approximately 1:9 to approximately 9:1, and the feeding ratio can be altered continuously within the aforementioned range. Detailed description of the ALD method will be described later.

As shown in FIG. 4C, a heat treatment process 17 is performed on the high-k dielectric film 16B for densification and to resolve oxygen shortage of the high-k dielectric film 16B. Herein, the heat treatment process 17 is performed by employing one from a group consisting of a furnace method, a rapid temperature process (RTP) method and a rapid temperature annealing (RTA) method. Herein, the heat treatment process 17 is performed in an atmosphere which includes a very small amount of O₃, Ar, N₃ or O₂. The heat treatment process 17 using O₃ is performed for approximately 10 seconds to approximately 120 seconds. The heat treatment process 17 using O₂ plasma is performed at a temperature ranging from approximately 100° C. to approximately 400° C. with a power ranging from approximately 100 W to approximately 1,000 W for approximately 10 seconds to approximately 60 seconds.

Furthermore, as shown in FIG. 4D, the second oxide layer 16C is formed on top of the high-k dielectric film 16B. Herein, the second oxide layer 16C is, just like the first oxide layer 16A, a high temperature oxide layer formed in a thickness ranging from approximately 30 Å to approximately 60 Å by employing a superior internal pressure and SiH₂Cl₂ and H₂O gases as source gases with a superior TDDB characteristic. Thus, the dielectric structure 16 is formed, including: the first oxide layer 16A; the high-k dielectric film 16B; and the second oxide layer 16C.

Moreover, as shown in FIG. 4E, the second polysilicon layer 18 for a control gate is formed on top of the dielectric structure 16. Herein, the second polysilicon layer 17 is, just like the first polysilicon layer 14, formed in a thickness of approximately 500 Å to approximately 2,000 Å by employing SiH₄ or Si₂H₆ and PH₃ gases.

Hereinafter, the aforementioned ALD method will be described in detail.

As shown in FIG. 5, the ALD process is performed in a sequential order of: Hf formation; N₂ purge; ozone (O₃) oxidation; N₂ purge; Al formation; N₂ purge; O₃ oxidation; and N₂ purge. In detail, a Hf source gas is implanted into an ALD chamber to form an Hf layer on a wafer, and then N_(2 gas) is supplied into the ALD chamber to purge the residual Hf source gas which was not used in the formation. Subsequently, O₃ gas is supplied into the ALD chamber for oxidizing the Hf layer to thereby form an HfO₂ thin film. Then, N₂ gas is supplied into the ALD chamber again to purge the residual O₃ gas which did not react. Next, an Al source gas is supplied in_(t)o the ALD chamber to form an Al layer on an entire surface of the above resulting wafer structure including the HfO₂ thin film, and then, N₂ gas is supplied to purge the residual Al source gas, which was not used in the formation. Then, O₃ gas is supplied into the ALD chamber for oxidizing the Al layer formed on top of the above resulting wafer structure to thereby form an Al₂O₃ layer, and then, N₂ gas is again supplied into the ALD chamber to purge the residual O₃ gas which did not react.

As shown in FIG. 6, the ALD process can be performed by another method in a sequential order of: Al formation; N₂ purge; O₃ oxidation; N₂ purge; Hf formation; N₂ purge; O₃ oxidation; and N₂ purge. In detail, an Al source gas is supplied into an ALD chamber to form an Al layer on a wafer, and then N₂ gas is supplied into the ALD chamber to purge the residual Al source gas which was not used in the formation. Subsequently, O₃ gas is supplied into the ALD chamber for oxidizing the Al layer to form an Al₂O₃ thin film. Then, N₂ gas is supplied again into the ALD chamber to purge the residual O₃ gas which did not react. Next, an Hf source gas is supplied into the ALD chamber to form a Hf layer on the above resulting wafer structure including the Al₂O₃ thin film, and then N₂ gas is supplied into the ALD chamber to purge the residual Hf source gas which was not used in the formation. Then, O₃ gas is supplied into the ALD chamber for oxidizing the Hf layer to form a HfO₂ film. Then N₂ gas is supplied again into the ALD chamber to purge the residual O₃ gas.

As shown in FIG. 7, the ALD process can be performed by still another method in a sequential order of: Hf—Al formation; N₂ purge; O₃ oxidation; and N₂ purge. That is, layers of Hf and Al are formed simultaneously, and then purge and oxidation processes are performed to form a Hfo₂Al₂O₃-based thin film.

Meantime, as shown in Table 1, the high-k dielectric film 16B can be formed of a material with a dielectric constant higher then the Al₂O₃ film (i.e., k>9) or a compound layer of such materials, other than the Al₂O₃ and HfO₂ layers.

The specific embodiments of the present invention described above only cover the case of a dielectric structure in a flash memory device. However, the flash memory device is one example of various applications. The embodiments of the present invention can be applied to other types of nonvolatile memory devices with a dielectric structure, including electrically erasable and programmable read only memory (EEPROM) and erasable and programmable read only memory (EPROM). The embodiments of the present invention can be also applied to fabrication processes of flash memory devices under 70 nm level, wherein a self-aligned-shallow trench isolation (SA-STI) process or a self-aligned floating gate (SAFG) is used.

In accordance with the specific embodiments of the present invention, the dielectric structure of a nonvolatile memory device such as the flash memory device is formed into the structure of: the first oxide layer; the high-k dielectric layer; and the second oxide layer. As a result, the coupling ratio required by the device is satisfied in accordance with the decreasing design rule as memory devices have become highly integrated, the superior leakage current characteristic is secured, and the reliability is improved.

The present application contains subject matter related to the Korean patent application No. KR 2005-0056952, filed in the Korean Patent Office on Jun. 29, 2005, the entire contents of which being incorporated herein by reference.

While the present invention has been described with respect to certain specific embodiments, it will be apparent to those skilled in the art that various changes and modifications may be made without departing from the spirit and scope of the invention as defined in the following claims. 

1. A dielectric structure in a nonvolatile memory device including a floating gate, the dielectric structure and a control gate, the dielectric structure comprising: a first oxide layer; a first high-k dielectric film formed on the first oxide layer, wherein the first high-k dielectric film includes one selected from materials with a dielectric constant of approximately 9 or higher and a compound of at least two of the materials; and a second oxide layer formed on the first high-k dielectric film.
 2. The dielectric structure of claim 1, further comprising: a second high-k dielectric film formed on the second oxide layer by employing a material identical to the first high-k dielectric film; and a third oxide layer formed on the second high-k dielectric film.
 3. The dielectric structure of claim 1, wherein the first high-k dielectric film includes a material chosen from a group consisting of aluminum oxide (Al₂O₃), yttrium oxide (Y₂O₃), hafnium oxide (HfO₂), and Zirconium oxide (ZrO2), each with a dielectric constant ranging from approximately 9 to
 25. 4. The dielectric structure of claim 1, wherein the first high-k dielectric film includes a material chosen from a group consisting of lanthanum oxide (La₂O₃), tantalum oxide (Ta₂O₅), and titanium oxide (TiO₂), each with a dielectric constant ranging from approximately 26 to
 80. 5. The dielectric structure of claim 2, wherein the first high-k dielectric film and the second high-k dielectric film include a material chosen from a group consisting of Al₂O₃, Y₂O₃, HfO₂, and ZrO₂, each with a dielectric constant ranging from approximately 9 to
 25. 6. The dielectric structure of claim 2, wherein the first high-k dielectric film and the second high-k dielectric film include a material chosen from a group consisting of La₂O₃, Ta₂O₅, and TiO₂, each with a dielectric constant ranging from approximately 26 to
 80. 7. The dielectric structure of claim 1, wherein the first high-k dielectric film includes a compound chosen from a group consisting of HfO_(x)Al_(y)O_(z), ZrO_(x)Al_(y)O_(z) and LaO_(x)Al_(y)O_(z), where x, y and z representing feeding ratios of atoms composing the individual compounds are 0 or a natural number.
 8. The dielectric structure of claim 2, wherein the first high-k dielectric film and the second high-k dielectric film include a compound selected from a group consisting of HfO_(x)Al_(y)O_(z), ZrO_(x)Al_(y)O_(z) and LaO_(x)Al_(y)O_(z), where x, y and z representing feeding ratios of atoms composing the individual compounds are 0 or a natural number.
 9. The dielectric structure of claim 7, wherein a feeding ratio of hafnium (Hf) to aluminum (Al) of the HfO_(x)Al_(y)O_(z) compound ranges from approximately 1:9 to approximately 9:1.
 10. The dielectric structure of claim 8, wherein a feeding ratio of Hf to Al of the HfO_(x)Al_(y)O_(Z) compound ranges from approximately 1:9 to approximately 9:1.
 11. The dielectric structure of claim 1, wherein the first high-k dielectric film is formed in a thickness ranging from approximately 30 Å to approximately 100 Å.
 12. The dielectric structure of claim 2, wherein the first high-k dielectric film and the second high-k dielectric film are formed in a thickness ranging from approximately 30 Å to approximately 100 Å.
 13. The dielectric structure of claim 2, wherein the first oxide layer to the third oxide layer are high temperature oxide layers formed by employing dichlorosilane (SiH₂Cl₂) and hydrogen oxide (H₂O) gases.
 14. The dielectric structure of claim 13, wherein the first oxide layer to the third oxide layer are formed in a thickness ranging from approximately 30 Å to approximately 60 Å. 15-36. (canceled) 